Title: Avaliação da resistência à fratura de raízes portadoras de pinos metálicos fundidos e de fibra-de-vidro com diferentes comprimentos, por meio do teste de compressão
Other Titles: Evaluation of the resistance to fracture of roots with cast metallic posts and fiber-glass posts at different working lengths, using the compression test
???metadata.dc.creator???: Giovani, Alessandro Rogério 
???metadata.dc.contributor.advisor1???: Paulino, Silvana Maria
???metadata.dc.description.resumo???: Neste estudo foi avaliada, in vitro, a resistência à fratura de raízes portadoras de retentores intra-radiculares de fibra-de-vidro e metálicos fundidos com diferentes comprimentos, por meio do teste de compressão. Sessenta caninos superiores hígidos tiveram as coroas seccionadas e os canais radiculares tratados endodonticamente. As raízes foram incluídas em blocos de resina, com exceção dos 4 mm cervicais. O espaço protético foi realizado com brocas cilíndricas, em baixa rotação, acopladas em paralelômetro, obtendo-se preparos com comprimentos de 6 mm (GI), 8 mm (GII) e 10 mm (GIII). Cada grupo foi subdividido em dois, de acordo com o tipo de pino utilizado: de fibra-de-vidro e metálico fundido, que foram cimentados com Panavia F. Coroas metálicas fundidas foram confeccionadas e cimentadas com cimento de fosfato de zinco. Os blocos de resina com as raízes foram posicionados na Máquina Universal de Ensaios de modo que uma ponta retangular de extremidade arredondada aplicasse uma força com angulação de 135o em relação ao longo eixo das raízes, com velocidade constante de 1 mm/min. O teste de Dunn mostrou não haver diferença significante (p>0,05) entre os pinos metálicos fundidos de 6 mm (0,91 kN), 8 mm (0,87 kN) e 10 mm (0,74 kN), em relação aos pinos de fibra-de-vidro, os de 8 mm (0,58 kN) foram estatisticamente semelhantes aos de 6 mm (0,43 kN) e aos de 10 mm (1,00 kN), enquanto que os de 6 mm e 10 mm foram estatisticamente diferentes entre si (p<0,01). Concluiu-se que os diferentes comprimentos podem interferir na resistência à fratura, dependendo do tipo de pino utilizado.
Abstract: In this study, it was evaluated, in vitro, the resistance of fracture roots with glass-fiber and metallic intraradicular retainers with different lengths, using the compression test. Sixty caries-free superior canines had their crowns sectioned and radicular canals endodontically treated. The roots were embedded in acrylic resin, except for the 4 mm of cervical area. The prosthetic space was performed with cylindrical bur in low speed attached to a parallelometer, obtaining prepares with length of 6 mm (GI), 8 mm (GII) and 10 mm (GIII). Each group was divided into 2 subgroups according to the post material: glass-fiber posts and metallic cast posts, which were luted with Panavia F cement. Metallic cast crowns made done and cemented with zinc phosphate. The resin/dentin blocks were positioned in the Instron 4444 Universal Machine, using a rectangular tip with round edge, in an angle of 135o in relation to the root long axis and at a speed of 1 mm/min. The Dunn test showed no significant difference (p>0.05) among the metallic posts of different length (6 mm 0.91 kN, 8 mm 0.87 kN and 10 mm 0.74 kN). Besides in the glass-fiber post group, there weren t significant difference among posts of 8 mm (0.58 kN) length, when compared to the 6 mm (0.43 kN) and 10 mm (1.00 kN). However, the post of 6 mm were statistically different (p<0.01) when compared with the 10 mm length. It was concluded that the post length influenced on the fracture resistance depending on the post type.
Keywords: Odontologia
Endodontia
Pinos pré-fabricados Fratura
Pinos metálicos fundidos Fratura
Título
Dentistry
Endodontics
Pre-fabricated posts Fracture
Cast metallic posts Fracture
Title
???metadata.dc.subject.cnpq???: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
Language: por
???metadata.dc.publisher.country???: BR
Publisher: Universidade de Ribeirão Preto
???metadata.dc.publisher.initials???: UNAERP
???metadata.dc.publisher.department???: Endodontia
???metadata.dc.publisher.program???: Pós-Graduação em Odontologia
Citation: GIOVANI, Alessandro Rogério. Evaluation of the resistance to fracture of roots with cast metallic posts and fiber-glass posts at different working lengths, using the compression test. 2007. 117 f. Dissertação (Mestrado em Endodontia) - Universidade de Ribeirão Preto, Ribeirão Preto, 2007.
???metadata.dc.rights???: Acesso Aberto
URI: http://tede.unaerp.br:8180//handle/tede/42
Issue Date: 27-Apr-2007
Appears in Collections:Pos-Graduacao_em_Odontologia

Files in This Item:
File Description SizeFormat 
ALESSANDRO ROGERIO GIOVANI.pdf2.06 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.