Title: Avaliação da retenção de pinos intra-radiculares fixados com cimento resinoso e de fosfato de zinco, em dentes obturados com cimento à base de óxido de zinco e eugenol, em diferentes períodos entre a obturação e preparo protético/ cimentação dos pinos
Other Titles: Evaluation of intra-radicular posts fixed with resin cement and zinc phosphate cement, in teeth sealed with zinc oxide and eugenol-based sealers, at different periods between the obturation and prosthetic preparation/post cementation
???metadata.dc.creator???: Dias, Larissa Lustosa Lima 
???metadata.dc.contributor.advisor1???: Paulino, Silvana Maria
First advisor-co: Floriam, Luis José
???metadata.dc.description.resumo???: Neste estudo foi avaliada, in vitro, a retenção de pinos intra-radiculares fixados com cimento resinoso e de fosfato de zinco, em dentes obturados com cimento à base de óxido de zinco e eugenol, em diferentes períodos de tempo entre a obturação e o procedimento de preparo do espaço protético e cimentação dos pinos, por meio do teste de tração. Sessenta caninos superiores tiveram as coroas seccionadas e as raízes incluídas em blocos de resina. Os espécimes foram distribuídos em 3 grupos, de acordo com os períodos de tempo entre a obturação e a cimentação dos pinos: GI imediato; GII 72 h e GIII 4 meses. Após preparo biomecânico e obturação dos canais com cimento à base de óxido de zinco e eugenol, os espaços protéticos foram preparados, respeitando-se os tempos propostos, com brocas cilíndricas em baixa rotação, acopladas a um paralelômetro. Cada grupo foi subdividido em dois, de acordo com o tipo de cimento utilizado na fixação dos pinos intra-radiculares: fosfato de zinco e Panavia. Decorridos os períodos experimentais, os corpos-de-prova foram submetidos ao teste de tração na Máquina Universal de Ensaios, à velocidade de 0,5mm/min, e os resultados submetidos à análise estatística. O teste de Tukey mostrou haver diferença significante (p<0,001) entre os valores de resistência à tração dos pinos fixados com cimento de fosfato de zinco (0,2112 kN) e Panavia (0,0501 kN); entretanto, não houve diferença significante (p>0,05) entre os diferentes períodos de tempo entre a obturação e cimentação dos pinos, independente do cimento utilizado. Concluiu-se que o cimento endodôntico à base de óxido de zinco e eugenol influenciou a resistência à tração dos pinos fixados com cimento resinoso, mas não interferiu nos diferentes períodos de tempo entre a obturação e o procedimento de preparo do espaço protético e cimentação dos pinos.
Abstract: In this study, it was evaluated in vitro the retention of intraradicular posts cemented with resinous sealer and zinc phosphate sealer, in teeth obtured with zinc oxide eugenol-based cement, in different periods between the obturation, preparation procedure of the prosthetic space and posts cementation, by means of tensile test. Sixty superior canines had the crowns sectioned and the roots embedded in resin blocks. The specimens were distributed into 3 groups, according to the periods between obturation and posts cementation: GI - immediate; GII - 72 hours and GIII - 4 months. After the biomechanical preparation and canals obturation with zinc oxide eugenol-based cement, the prosthetic spaces were prepared with cylindrical drills in low rotation, connected to a paralelometer, respecting the considered times. Each group was subdivided in two groups, according to the type of sealer used during intraradicular posts cementation: zinc phosphate and Panavia F. Following the experimental periods, the specimens were submitted to the tensile test in the Universal Test Machine, at a speed of 0.5 mm/min, and the results were submitted to the statistical analysis. The Tukey test showed significant difference (p<0.001) between tensile strength values of the posts cemented with zinc phosphate sealer (0.2112 kN) and Panavia F (0.0501 kN); however, no significant differences (p>0.05) were observed between the obturation periods and posts cementation, regardless of the cement. It was concluded that the endodontic zinc oxide eugenol-based cement influenced the tensile strength of the posts cemented with resinous sealer, but did not interfere with the different periods between the obturation, preparation procedure of the prosthetic space and posts cementation.
Keywords: Odontologia
Endodontia
Materiais restauradores
Cimentos resinosos
Dentistry
Endodontics
Restaurative materials
Resin cements
???metadata.dc.subject.cnpq???: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
Language: por
???metadata.dc.publisher.country???: BR
Publisher: Universidade de Ribeirão Preto
???metadata.dc.publisher.initials???: UNAERP
???metadata.dc.publisher.department???: Endodontia
???metadata.dc.publisher.program???: Pós-Graduação em Odontologia
Citation: DIAS, Larissa Lustosa Lima. Evaluation of intra-radicular posts fixed with resin cement and zinc phosphate cement, in teeth sealed with zinc oxide and eugenol-based sealers, at different periods between the obturation and prosthetic preparation/post cementation. 2007. 100 f. Dissertação (Mestrado em Endodontia) - Universidade de Ribeirão Preto, Ribeirão Preto, 2007.
???metadata.dc.rights???: Acesso Aberto
URI: http://tede.unaerp.br:8180//handle/tede/41
Issue Date: 29-Jun-2007
Appears in Collections:Pos-Graduacao_em_Odontologia

Files in This Item:
File Description SizeFormat 
LARISSA LUSTOSA LIMA DIAS.pdf5.64 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.