???metadata.dc.type???: Dissertação
Title: Avaliação da solubilidade do cimento obturador Epiphany preparado com solvente resinoso
Other Titles: Evaluation of the solubility of the Epiphany sealer prepared with resin solvent
???metadata.dc.creator???: Mathias Junior, Odival 
???metadata.dc.contributor.advisor1???: Sousa Neto, Manoel D.
???metadata.dc.description.resumo???: O objetivo do presente estudo foi avaliar a solubilidade, seguindo a Especificação nº 57 da ANSI/ADA, com redução de 80 % do volume dos corpos-de-prova, do cimento Epiphany em diferentes condições experimentais: GI. Epiphany sem fotoativação, GII. Epiphany preparado com solvente resinoso sem fotoativação, GIII. Epiphany fotoativado, GIV. Epiphany preparado com solvente rsinoso e fotoativado. Dez corposde- prova do cimento de cada grupo, com 1,5 mm de espessura e 7,75 mm de diâmetro, foram obtidos a partir de moldes de teflon. Os corpos-de-prova tiveram sua massa pesada (em gramas) e foram imersos, dois a dois, em 7,5 mL de água destilada por sete dias. Após este período foram removidos, secos e pesados novamente. A solubilidade foi considerada como a perda de massa de cada amostra, expressa como porcentagem da massa original. Os líquidos de imersão das amostras foram submetidos à espectrometria. Para tanto, cápsulas calcinadas foram queimadas a 550 °C e pesadas, em seguida adicionou-se em cada cápsula 50 mL da água onde cada cimento foi imerso, e estas foram levadas a 550 °C e novamente pesadas. Cinzas contidas nas cápsulas foram diluídas em água destilada para verificação da presença dos ions de Ca2+, Mg2+, Fe2+, Zn2+, Ni2+ e Na+. O teste de Tukey evidenciou que, em relação à solubilidade (%), os cimentos não fotoativados foram estatisticamente semelhantes entre si (GI = 6,93 % e GII = 6,39 %) (p>0,05) e diferentes dos cimentos fotoativados, que também apresentaram-se estatisticamente diferentes entre si (p<0, 001) (GIII = 3,56 % e GIV = 0,47 %). Somente o cimento Epiphany preparado com solvente resinoso e fotoativado apresentou valores de solubilidade dentro dos padrões estabelecidos pela ANSI/ADA, liberando as seguintes quantidades de ions: 114,43 &#956;g Ca2+/mL, 2,4 &#956;g Mg2+/mL, 0,33 &#956;g Fe2+/mL, 0,11 &#956;g Zn2+/mL, 1,31 &#956;g Ni2+/mL e 7,1 &#956;g Na+/mL. Concluiu-se que o cimento Epiphany preparado com solvente resinoso, seguido de fotoativação, resultou em um cimento com baixo índice de solubilidade e expressiva liberação de ions cálcio.
Abstract: The purpose of this study was to evaluate the solubility of the Epiphany cement with 80% reduction in volume of the specimen s dimensions, based on ANSI/ADA Specification no. 57. The specimens were prepared in different experimental conditions: GI. Epiphany without photoactivation, GII. Epiphany prepared with resinous solvent without photoactivation, GIII. Epiphany followed by photoactivation, GIV. Epiphany prepared with resinous solvent followed by photoactivation. Ten specimens of each group (1.5 mm thickness and 7.75 mm diameter) were obtained from Teflon molds. The samples were weighted and immersed in distilled water for 7 days. After this period, they were removed, dried and weighed again. Solubility was calculated using samples weight loss (%). The immersion liquid was evaluated through atomic absorption spectrometry. For this purpose, capsules were burned at 550°C, weighted and 50 mL of water was added in capsules where each cement was immersed. The sets were submitted to 550°C and weighted. Ashes, contained in capsules, were diluted in water distilled to observe the presence of Ca2+, Mg2+, Fe2+, Zn2+, Ni2+ and Na+ions. Tukey test evidenced that the cements without photoactivation were statistically similar (p>0.05) between themselves (GI = 6.93 % and GII = 6.39 %) and different from the nonphotoactivated cements, which were statistically different (p<0.001) (GIII = 3.56% and GIV = 0.47%). Only the Epiphany cement prepared with resinous solvent followed by photoactivation presented solubility values within ANSI/ADA requirements, liberating the following amounts of ions: 114.43 &#956;g Ca2+/mL, 2.4 &#956;g Mg2+/mL, 0.33 &#956;g Fe2+/mL, 0.11 &#956;g Zn2+/mL, 1.31 &#956;g Ni2+/mL and 7.1 &#956;g N+a/mL. It was concluded that the association of Thinning to the Epiphany cement followed by polymerization resulted in a cement with low solubility and expressive liberation of calcium ions.
Keywords: Odontologia
Endodontia
Canal Radicular
Dentistry
Endodontics
Root canal
???metadata.dc.subject.cnpq???: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
Language: por
???metadata.dc.publisher.country???: BR
Publisher: Universidade de Ribeirão Preto
???metadata.dc.publisher.initials???: UNAERP
???metadata.dc.publisher.department???: Endodontia
???metadata.dc.publisher.program???: Pós-Graduação em Odontologia
Citation: MATHIAS JUNIOR, Odival. Evaluation of the solubility of the Epiphany sealer prepared with resin solvent. 2008. 87 f. Dissertação (Mestrado em Endodontia) - Universidade de Ribeirão Preto, Ribeirão Preto, 2008.
???metadata.dc.rights???: Acesso Aberto
URI: http://tede.unaerp.br:8180//handle/tede/37
Issue Date: 27-Feb-2008
Appears in Collections:Pos-Graduacao_em_Odontologia

Files in This Item:
File Description SizeFormat 
ODIVAL MATHIAS JR.pdf2.91 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.